Water Based Epoxy Resin Fast Drying Anti Corrosion Waterborne Epoxy Resin

2k Water Based Epoxy Resin Fast Drying Anti Corrosion Waterborne Epoxy Resin

                                                                            WL-213 Waterborne Epoxy Resin
 
 
Physical Property:
 

 
 
Performance:

• Non-ionic self-emulsifying type
• Small emulsion particle size
• Good film forming performance
• Low VOC content

• Epoxy gray paint performance

• Carbon steel plate (sand paper polishing)

◆ 80℃ X 120 minutes flash dry
◆ 14 days natural dry curing period
◆ Film thickness 50~60μm
◆ Salt spray resistance>800hrs
 
 
 

• Epoxy varnish performance comparison
• Alkali resistance performance:

• 23-29um, baking at 80℃ for 30 minutes,
  0.1mol/L NaOH aqueous solution
  After 64h of alkali resistance testing :

               
 
 
Has spots                                                             Almost no spots
(AP resin)                                                            (WL-213/WL-140)
 

• Acid resistance:

Thickness of film is 23-29um, back at 80℃ for 30 minutes,
0.1mol/L H2SO4 aqueous solution
                
 
Large bubbles on the board                    Small bubbles or no bubbles
( AP resin)                                                     (WL-213/WL-140)
 
 
3.Epoxy white paint performance comparison

• Ethanol wiping Resistance performance:

Thickness of film is 23-26um, back at 80℃ for 30 minutes

Failed after 30 wipes                                                              Pass after 50 wipes
(Contrast resin)                                                                      (WL-213/WL-140)
 

• Alkali resistance performance:

The film thickness all is 23-29um, after 80℃X30 minutes
Put it into 0.1mol/L NaOH aqueous solution and soak for 64 hours
The paint surface of WL-213/WL-140 is slightly dull
The paint surface of the contrast resin has more large bubbles
 
After 64h of alkali resistance testing :

 
        ( AP resin)                                                                         (WL-213/WL-140)
 
 

• Acid resistance performance:

-The thickness of the film is 23-29um, after drying at 80℃ for 30 minutes
-Put into 0.1mol/L sulfuric acid aqueous solution
-After 64 hours of soaking
-The paint surface of WL-213/WL-140 is slightly dull
-The paint surface of the contrast resin has large bubbles and cracks
 
    
       ( contrast resin)                                                                             (WL-213/WL-140)
 
 

• Salt spray resistance performance:

-The film thickness is 50-60um
-Test after 7 days in a constant temperature and humidity environment
-After 64 hours of salt spray resistance test, the white paint board of the contrast resin is corroded more

           ( contrast resin)                                                          (WL-213/WL-140)
 
 
Special Tips
This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.